Histological evaluation of titanium fiber mesh-coated implants in a rabbit femoral condyle model.

Abstract

<h4>Objectives</h4>This study was aimed to comparatively evaluate new bone formation into the pores of a flexible titanium fiber mesh (TFM) applied on the surface of implant.<h4>Methods</h4>Twenty-eight custom made cylindrical titanium implants (4 ×10 mm) with and without a layer of two different types of TFM (fiber diameter of 22 µm and 50 µm, volumetric porosity ~70%) were manufactured and installed bilaterally in the femoral condyles of 14 rabbits. The elastic modulus for these two TFM types was ~20 GPa and ~5 GPa respectively, whereas the solid titanium was ~110 GPa. The implants (Control, TFM-22, TFM-50) were retrieved after 14 weeks of healing and prepared for histological assessment. The percentage of the bone area (BA%), the bone-to-implant contact (BIC%) and amount were determined.<h4>Results</h4>Newly formed bone into mesh porosity was observed for all three types of implants. Histomorphometric analyses revealed significantly higher (~2.5 fold) BA% values for TFM-22 implants (30.9 ± 9.5%) compared to Control implants (12.7 ± 6.0%), whereas BA% for TMF-50 did not significantly differ compared with Control implants. Furthermore, both TFM-22 and TFM-50 implants showed significantly higher BIC% values (64.9 ± 14.0%, ~2.5 fold; 47.1 ± 14.1%, ~2 fold) compared to Control (23.6 ± 17.4%). Finally, TFM-22 implants showed more and thicker trabeculae in the peri-implant region.<h4>Significance</h4>This in vivo study demonstrated that implants with a flexible coating of TFM improve bone formation within the inter-fiber space and the peri-implant region.